UNS S31653 / 316LN Austenitic Stainless Steel Pipe Seamless 1 - 48 Inch Size

Categories Austenitic Stainless Steel Pipe
Brand Name: TOBO
Model Number: UNS S31653
Certification: SGS/BV/ABS/LR/TUV/DNV/BIS/API/PED
Place of Origin: China
MOQ: 1 pc
Price: Negotiation
Payment Terms: L/C, T/T, Western Union
Supply Ability: 10000PC/Month
Delivery Time: 35 working days
Packaging Details: In bundles, ply-wooden case
Product Name: Stainless steel Pipe
Product Type: Seamless
Size: 1-48 inch
Material Grrade: 316LN(UNS S31653)
Type: Round Pipe
Standard: DIN,EN,ASTM,BS,JIS,GB,etc.
Application: Orthopaedic implants/Trauma nails/ Neurological applications/Surgical instrument
Thickness: 0.4-30mm,1.0mm,0.4-30mm or customized,Sch5S-SchXXS,0.3-30
Company Info.
TOBO STEEL GROUP CHINA
Verified Supplier
View Contact Details
Product List
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    UNS S31653 / 316LN Austenitic Stainless Steel Pipe Seamless 1 - 48 Inch Size

    UNS S31653 / 316LN Austenitic Stainless Steel Pipe: (UNS S31653)


    316LN (UNS S31653) is a low-carbon, nitrogen-enhanced version of Type 316 molybdenum-bearing austenitic stainless steel. The Type 316 alloys are more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels such as Type 304. They also offer higher creep, stress-rupture and tensile strength at elevated temperature. The nitrogen in Type 316LN adds additional resistance to sensitization in some circumstances.

    The nitrogen content of Type 316LN stainless steel also provides some solid solution hardening, raising its minimum specified yield strength compared to Type 316L stainless steel. Like Types 316 and 316L, the Type 316LN alloy also offers good resistance to general corrosion and pitting/crevice corrosion.



    Typical Manufacturing Specifications

    ASTM F138

    ASTM F2181

    Also individual customer specifications.


    Detailed Specifictions

    1. Stainless steel Pipes

    2. sch5s-schxxs
    3. ISO9001,ISO9000
    4. Market:America,Africa,Middle East,Southeast of Asia

    Product TypeStainless steel Pipes
    StandardASTM F138
    Size1/2’’~48’’(Seamless);16’’~72’’(Welded)
    Wall thicknessSch5~Sch160XXS
    Manufacturing processPush, Press, Forge, Cast, etc.
    MaterialCarbon steel, stainless steel, alloy steel, duplex stainless, nickel alloy steel
    Carbon steelASTM A234 WPB, WPC;
    Stainless steel

    304/SUS304/UNS S30400/1.4301

    304L/UNS S30403/1.4306;

    304H/UNS S30409/1.4948;

    309S/UNS S30908/1.4833

    309H/UNS S30909;

    310S/UNS S31008/1.4845;

    310H/UNS S31009;

    316/UNS S31600/1.4401;

    316Ti/UNS S31635/1.4571;

    316H/UNS S31609/1.4436;

    316L/UNS S31603/1.4404;

    316LN/UNS S31653;

    317/UNS S31700;

    317L/UNS S31703/1.4438;

    321/UNS S32100/1.4541;

    321H/UNS S32109;

    347/UNS S34700/1.4550;

    347H/UNS S34709/1.4912;

    348/UNS S34800;

    Alloy steel

    ASTM A234 WP5/WP9/WP11/WP12/WP22/WP91;

    ASTM A860 WPHY42/WPHY52/WPHY60/WPHY65;

    ASTM A420 WPL3/WPL6/WPL9;

    Duplex steel

    ASTM A182 F51/S31803/1.4462;

    ASTM A182 F53/S2507/S32750/1.4401;

    ASTM A182 F55/S32760/1.4501/Zeron 100;

    2205/F60/S32205;

    ASTM A182 F44/S31254/254SMO/1.4547;

    17-4PH/S17400/1.4542/SUS630/AISI630;

    F904L/NO8904/1.4539;

    725LN/310MoLN/S31050/1.4466

    253MA/S30815/1.4835;

    Nickel alloy steel

    Alloy 200/Nickel 200/NO2200/2.4066/ASTM B366 WPN;

    Alloy 201/Nickel 201/NO2201/2.4068/ASTM B366 WPNL;

    Alloy 400/Monel 400/NO4400/NS111/2.4360/ASTM B366 WPNC;

    Alloy K-500/Monel K-500/NO5500/2.475;

    Alloy 600/Inconel 600/NO6600/NS333/2.4816;

    Alloy 601/Inconel 601/NO6001/2.4851;

    Alloy 625/Inconel 625/NO6625/NS336/2.4856;

    Alloy 718/Inconel 718/NO7718/GH169/GH4169/2.4668;

    Alloy 800/Incoloy 800/NO8800/1.4876;

    Alloy 800H/Incoloy 800H/NO8810/1.4958;

    Alloy 800HT/Incoloy 800HT/NO8811/1.4959;

    Alloy 825/Incoloy 825/NO8825/2.4858/NS142;

    Alloy 925/Incoloy 925/NO9925;

    Hastelloy C/Alloy C/NO6003/2.4869/NS333;

    Alloy C-276/Hastelloy C-276/N10276/2.4819;

    Alloy C-4/Hastelloy C-4/NO6455/NS335/2.4610;

    Alloy C-22/Hastelloy C-22/NO6022/2.4602;

    Alloy C-2000/Hastelloy C-2000/NO6200/2.4675;

    Alloy B/Hastelloy B/NS321/N10001;

    Alloy B-2/Hastelloy B-2/N10665/NS322/2.4617;

    Alloy B-3/Hastelloy B-3/N10675/2.4600;

    Alloy X/Hastelloy X/NO6002/2.4665;

    Alloy G-30/Hastelloy G-30/NO6030/2.4603;

    Alloy X-750/Inconel X-750/NO7750/GH145/2.4669;

    Alloy 20/Carpenter 20Cb3/NO8020/NS312/2.4660;

    Alloy 31/NO8031/1.4562;

    Alloy 901/NO9901/1.4898;

    Incoloy 25-6Mo/NO8926/1.4529/Incoloy 926/Alloy 926;

    Inconel 783/UNS R30783;

    NAS 254NM/NO8367;

    Monel 30C

    Nimonic 80A/Nickel Alloy 80a/UNS N07080/NA20/2.4631/2.4952

    Nimonic 263/NO7263

    Nimonic 90/UNS NO7090;

    Incoloy 907/GH907;

    Nitronic 60/Alloy 218/UNS S21800

    PackageWooden cases, pallets, nylon bags or according to the customers' requirements
    MOQ1pcs
    Delivery time10-100 days depending on quantity
    Payment termsT/T or Western Union or LC
    ShipmentFOB Tianjin/Shanghai, CFR, CIF, etc
    ApplicationPetroleum/Power/Chemical/Construction/Gas/Metallurgy/Shipbuilding etc
    RemarksOther materials and drawings are available.
    Welcome to contact us.

    5. COMPOSITION

    ElementMinimum*Maximum*
    Chromium16.018.0
    Molybdenum2.003.00
    Nickel10.014.0
    Phosphorus0.045
    Sulfur0.030
    Silicon0.75
    Carbon0.030
    Nitrogen0.16
    Manganese2.00
    Ironbalance

    6.PHYSICAL PROPERTIES

    PropertyValueUnits
    Density at 72°F(22℃)

    8.00

    0.289

    g/cm³

    Lb/in³

    Melting Range2450°F-2630°F1345℃-1440℃
    Thermal Conductivity at 212°F(100℃)

    8.4

    14.6

    BTU/hr·ft·°F

    W/m·K

    Thermal Expansion

    Coefficient at 68-212°F(20-100℃)

    9.2

    16.5

    μ in/in/°F

    μ m/m/°C

    Thermal Expansion

    Coefficient at 68-932°F(20-500℃)

    10.1

    18.2

    μ in/in/°F

    μ m/m/°C

    Thermal Expansion

    Coefficient at 68-1832°F(20-1000℃)

    10.8

    19.5

    μ in/in/°F

    μ m/m/°C


    Available Tube Product form

    Straight

    Coiled

    Seamless


    Typical Applications

    Orthopaedic implants

    Trauma nails

    Neurological applications

    Surgical instruments


    Industries predominantly using this Grade

    Chemical processing

    High performance liquid chromatography (hplc)

    Medical


    316LN stainless is a single phase austenitic (face centered cubic) stainless steel at all temperatures up to the melting point. The alloy can not be hardened by heat treatment. The alloy is nonmagnetic in the annealed condition. Its magnetic permeability is typically less than 1.02 at 200 H (Oersteds). Permeability values for cold de-formed material vary with composition and the amount of cold deformation, but are usually higher than that for annealed material.


    7.MECHANICAL PROPERTIES


    Typical Room Temperature properties

    PropertyASTM A 240
    Yield Strength, 0.2% offset

    30 ksi*

    205 MPa*

    Ultimate Tensile Strength

    75 ksi*

    515 MPa*

    Elongation in 2" (51 mm)40%*
    Hardness217 Brinell** 95 HRB**

    * minimum, ** maximum


    Fatigue Resistance


    The fatigue strength or endurance limit is the maximum stress below which a material is unlikely to fail in 10 million cycles in an air environment. For austenitic stainless steels as a group, the fatigue strength is typically about 35 percent of the tensile strength. However, substantial variability in service results is experienced since additional variables such as corrosive conditions, type of loading and mean stress, surface condition, and other factors affect fatigue properties. For this reason, no definitive endurance limit value can be given which is representative of all operating conditions.


    OXIDATION RESISTANCE


    316LN alloy exhibits excellent resistance to oxidation and a low rate of scaling in air atmospheres at temperatures up to 1600- 1650°F (870-900°C). The performance of ATI 316LN stainless is slightly inferior to that of ATI 304 stainless steel, which has slightly higher chromium content (18% vs. 16% for ATI 316LN stainless). The rate of oxidation is greatly influenced by the atmosphere en-countered in service and by operating conditions. For this reason, no data can be presented that is applicable to all service conditions.


    Like other molybdenum bearing alloys, ATI 316LN stainless is subject to catastrophic oxidation at high temperatures in stagnant air atmospheres, such as in the heat treatment of closely packed items. This occurs due to the formation of low melting molybdenum trioxide (MoO3), which reacts with the alloy causing deep pitting and metal loss. When air is allowed to circulate, the MoO3 will evaporate from the metal surface and excessive oxidation is avoided.


    CORROSION PROPERTIES


    General Corrosion Resistance


    The molybdenum bearing grades such as ATI 316 and ATI 316LN stainless steels are more resistant to atmospheric and other mild types of corrosion than the 18Cr-8Ni stainless steels. In general, media that do not corrode 18-8 stainless steels will not attack the molybdenum-containing grades. One known exception is highly oxidizing acids such as nitric acid to which the molybdenum bearing stainless steels are less resistant. ATI 316 and ATI 316LN stainless are considerably more resistant than any of the other chromium-nickel types to solutions of sulfuric acid. Where condensation of sulfur-bearing gases occurs, these alloys are much more resistant than other types of stainless steels. In sulfuric acid solutions, the acid concentration has a strong influence on the rate of attack.


    Pitting Corrosion


    Resistance of austenitic stainless steels to pitting and/ or crevice corrosion in the presence of chloride or other halide ions is enhanced by higher chromium (Cr) and molybdenum (Mo) content. A relative measure of pitting resistance is given by the PREN (Pitting Resistance Equivalent with nitrogen) calculation, where:


    PREN = Cr + 3.3Mo +16N


    The PREN of ATI 316LN alloy (25.0) is higher than that of ATI 304 (PREN =20.0), reflecting the better pitting resistance which ATI 316LN alloy offers due to its Mo and N content. ATI 304 stainless steel is considered to resist pitting and crevice corrosion in waters containing up to about 100 ppm chloride. ATI 316LN alloy on the other hand, due to its Mo-content, will handle waters with up to about 2000 ppm chloride. This alloy is not recommended for use in seawater (~19,000 ppm chloride). ATI 316LN alloy is considered adequate for some applications that are exposed to salt spray. ATI 316LN stainless steel exhibits no evidence of corrosion in the 100-hour, 5% salt spray (ASTM B117) test.


    Intergranular Corrosion


    ATI 316 stainless steel is susceptible to precipitation of chromium carbides in grain boundaries when exposed to temperatures in the 800°F to 1500°F (425°C to 815°C) range. Such “sensitized” steels are subject to inter-granular corrosion when exposed to aggressive environments. ATI 316L alloy is available to avoid the hazard of intergranular corrosion. ATI 316L alloy provides resistance to intergranular attack even after short periods of exposure in the 800-1500°F (425-815°C) temperature range. Stress relieving treatments falling within these limits can be employed without affecting the corrosion resistance of the metal. Accelerated cooling from higher temperatures for the “L” grades is not needed when very heavy or bulky sections have been annealed. ATI 316LN alloy possesses the same mechanical properties as the corresponding higher-carbon ATI 316, and offers the resistance to intergranular corrosion of ATI 316L alloy. Although the short duration heating encountered during welding or stress relieving does not produce susceptibility to intergranular corrosion, continuous or prolonged exposure at 800-1200°F (422- 650°C) can produce sensitization of ATI 316LN (and of ATI 316L) stainless steels.


    The influence of molybdenum reduces the resistance of ATI 316LN stainless steel to highly oxidizing environments including the nitric acid environment of the ASTM A 262 practice C "Huey" test.


    Stress Corrosion Cracking


    Austenitic stainless steels are susceptible to stress corrosion cracking (SCC) in halide environments. Although the ATI 316, ATI 316L and ATI 316Ti alloys are more resistant to SCC than the 18 Cr-8 Ni alloys, they still are quite susceptible. Conditions that produce SCC are:


    (1) Presence of halide ion (generally chloride),

    (2) Residual tensile stresses, and

    (3) Temperature in excess of about 140°F (60°C)


    Stresses result from cold deformation or thermal cycles during welding. Annealing or stress relieving heat treatments may be effective in reducing stresses, thereby reducing sensitivity to halide SCC. Although the low carbon ATI 316L and ATI 316LN alloys offer no advantage as regards SCC resistance, they are better choices for service in the stress relieved condition in environments which might cause intergranular corrosion. If SCC resistance is desired, use of duplex stainless steels such as ATI 2205™ or ATI 2003® duplex stainless alloys should be considered.


    FABRICATING AND WELDING


    Fabrication


    The austenitic stainless steels, including the ATI 316LN alloy, are routinely fabricated into a variety of shapes ranging from the very simple to very complex. These alloys are blanked, pierced, and formed on equipment essentially the same as used for carbon steel. The excellent ductility of the austenitic alloys allows them to be readily formed by bending, stretching, deep drawing and spinning. However, because of their greater strength and work hardenability, the power requirements for the austenitic grades during forming operations are considerably greater than for carbon steels. Attention to lubrication during forming of the austenitic alloys is essential to accommodate the high strength and galling tendency of these alloys.


    Annealing


    The austenitic stainless steels are provided in the mill-annealed condition ready for use. Heat treatment may be necessary during or after fabrication to remove the effects of cold forming or to dissolve precipitated chromium carbides resulting from thermal exposures. For the ATI 316LN alloy the solution anneal is accomplished by heating in the 1900- 2150°F (1040-1175°C) temperature range followed by air cooling or a water quench, depending on section thickness. ATI 316LN stainless cannot be hardened by heat treatment.


    Welding


    The austenitic stainless steels are considered the most weldable of the stainless steels. They are routinely joined by all fusion and resistance welding processes. Two important considerations for weld joints in these alloys are (1) avoidance of solidification cracking, and (2) preservation of corrosion resistance of the weld and heat-affected zones. ATI 316LN stainless steel often is welded autogenously. If filler metal must be used for welding ATI 316LN stainless, it is advisable to utilize the low carbon ATI 316L or E318 filler metals. Contamination of the weld region with copper or zinc should be avoided, since these elements can form low melting point compounds, which in turn can create weld cracking.



    Quality UNS S31653 / 316LN Austenitic Stainless Steel Pipe Seamless 1 - 48 Inch Size for sale
    Send your message to this supplier
     
    From:
    To: TOBO STEEL GROUP CHINA
    Subject:
    Message:
    Characters Remaining: (0/3000)
     
    Inquiry Cart 0

    Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

    Copyright © 2009 - 2019 7cha.net. All rights reserved.